Home / Rubber Sheeting / NBR/PVC Rubber Sheeting / Black Fuel Resistant Nitrile/PVC 65° shore

Item Code: SM175

Black Fuel Resistant Nitrile/PVC 65° shore

SM175 Black Premium Grade Nitrile/PVC 65° shore is a Fuel Resistant Grade, High Quality 65°shore NBR/PVC sheeting.

N.B. Metroseal Sheeting can be supplied plain or with self adhesive backed tape (SAB). Rubber Strip to bespoke sizes are available along with customised sheets/gaskets. Please email your enquiry details to sales@metroseal.co.uk

  • Material Profile: see below for exact specifications
  • Thickness: 0.5mm to 50mm
  • Sheet Size: 1.4m wide in 5, 10 and 20m rolls
  • Finish: Plate finish
  • Cutting: Standard press-tools

This Product is REACH, RoHS, PAH and CE Compliant

Other grades, colours and finishes are available – subject to minimum batch quantities

PROPERTIES TEST METHOD VALUES FPS UNITS TEST METHOD VALUES METRIC UNITS
SPECIFIC GRAVITY ASTM D297 1.25 DIN 53508 1.25
HARDNESS ASTM D2240 65 ± 5 SH A DIN 53505 65 ± 5 SH A
TENSILE STRENGTH ( MIN ) ASTM D412 995 PSI DIN 53504 60 KG/CM2
ELONGATION AT BREAK ( MIN ) ASTM D412 250% DIN 53504 250%
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) ASTM D395 METHOD B

 

35%

 

DIN 53517

 

35%

ABRASION LOSS (MAX) ASTM D 5963 300 MM3 DIN 53516 300 MM3
TEAR RESISTANCE ( ANGULAR ) MIN ASTM D624 123 LBS/INCH DIN 53515 22 KG/CM
CHANGE IN PROPERTIES        
HEAT AGEING ( 72 HRS. AT 70ºC ) ASTM D 573      
— HARDNESS (PTS)   + 6 (MAX)   + 6 (MAX)
— TENSILE STRENGTH (%)   + 10 / -10   + 10 / -10
— ELONGATION AT BREAK (%)   + 10 / -20   + 10 / -20
VOLUME SWELL : AT 70ºC FOR 72 HRS/IN ASTM D 471      
ASTM OIL NO.1   -2%   -2%
ASTM OIL NO.2   + 4%   + 4%
ASTM OIL NO.3   + 13%   + 13%
AT FUEL B /24 HRS/ROOM TEMP, MAX   + 25 %   + 25 %
POLYMER CONTENT (NITRILE/PVC BLEND)   BLEND   BLEND
CHEMICAL RESISTANCE        
— OZONE ASTM D 1149 GOOD   GOOD
— DILUTE ACIDS AND BASES   GOOD   GOOD
— CONCENTRATED ACIDS AND BASES   NOT RECOMMENDED   NOT RECOMMENDED
— OILS   EXCELLENT   EXCELLENT