Home / Sheeting / SBR / EPDM / Black EPDM / SBR Rubber 70° shore
Common Era, Reach Compliance, RoHS Compliant, Technischer Überwachungsverein logos

Item Code: SM108

Black EPDM / SBR Rubber 70° shore

SM108 Black EPDM (10% content) / SBR Rubber 70° shore. It is used where a cheaper quality material will suit – in simple applications such as packing pieces, dust seals, protection pads etc where the material is not coming under any duress and slight resistance is required

This product is fully CE, PAH, RoHS, REACH compliant

  • Material Profile: See Below
  • Thickness: 1.5 mm to 50mm
  • Sheet Size: 1.4m wide in 5, 10 and 20m rolls
  • Finish: Smooth finish,
  • Cutting: Standard press-tools

Other grades, colours and finishes are available – subject to minimum batch quantities

Propertiestest method
values
fps units
test method
values
metric units
SPECIFIC GRAVITYDIN 535081.45 ± 0.05ASTM D2971.45 ± 0.05
HARDNESSDIN 5350570 ± 5 Sh AASTM D224070 ± 5 Sh A
TENSILE STRENGTH ( min )DIN 53504569 PSIASTM D41240 kg/cm2
ELONGATION AT BREAK ( min )DIN 53504200%ASTM D412200%
COMPRESSION SET (70 ºC/24 hrs/25% set) (max)DIN ISO 815-1 50%ASTM D395 METHOD B50%
TEAR RESISTANCE ( Angular ) minDIN 53515100 Lbs/InchASTM D62418 Kg/cm
CHANGE IN PROPERTIES
HEAT AGEING ( 72 hrs. AT 70 ºC )ASTM D573
--- HARDNESS (Pts)+ 5 (Max)+ 5 (Max)
--- TENSILE STRENGTH (%)± 20 (Max)± 20 (Max)
--- ELONGATION AT BREAK (%)± 30 (Max)± 30 (Max)
VOLUME SWELL : AT 70º C FOR 72 HRS/INASTM D 471
IRM OIL NO.1NOT RECOMMENDEDNOT RECOMMENDED
IRM OIL NO.2NOT RECOMMENDEDNOT RECOMMENDED
IRM OIL NO.3NOT RECOMMENDEDNOT RECOMMENDED
POLYMER CONTENT (EPDM)10%10%
CHEMICAL RESISTANCE
--- OZONEFAIRASTM D 1149FAIR
--- DILUTE ACIDS AND BASESFAIRFAIR
--- CONCENTRATED ACIDS AND BASES NOT RECOMMENDED NOT RECOMMENDED
--- OILS NOT RECOMMENDED NOT RECOMMENDED
--- SOLVENTS NOT RECOMMENDED NOT RECOMMENDED
TEMPERATURE RANGE-30 º to +90º C-30 º to +90º C
COLOURBLACKBLACK