Home / Sheeting / EPDM / Black EPDM / SBR Rubber 50° shore
rubber sheet

Item Code: SM105

Black EPDM / SBR Rubber 50° shore

M105 Black EPDM (10% content) / SBR Rubber 50° shore. It is used where a cheaper quality material will suit – in simple applications such as packing pieces, dust seals, protection pads etc where the material is not coming under any duress and slight resistance is required

This product is fully CE, PAH, RoHS, REACH compliant

  • Material Profile: See Below
  • Thickness: 1.5 mm to 50mm
  • Sheet Size: 1.4m wide in 5, 10 and 20m rolls
  • Finish: Smooth finish,
  • Cutting: Standard press-tools

Other grades, colours and finishes are available – subject to minimum batch quantities

Properties test method
values
fps units
test method
values
metric units
SPECIFIC GRAVITY DIN 53508 1.45 ± 0.05 ASTM D297 1.45 ± 0.05
HARDNESS DIN 53505 50 ± 5 Sh A ASTM D2240 50 ± 5 Sh A
Tensile Strength (Kg/cm2) DIN 53504 569 PSI ASTM D412 40 kg/cm2
ELONGATION AT BREAK ( min ) DIN 53504 200% ASTM D412 200%
COMPRESSION SET (70 ºC/24 hrs/25% set) (max) DIN 53517 50% ASTM D395 METHOD B 50%
TEAR RESISTANCE ( Angular ) min DIN 53515 100 Lbs/Inch ASTM D624 18 Kg/cm
CHANGE IN PROPERTIES
HEAT AGEING ( 72 hrs. AT 70 ºC ) ASTM D573
--- HARDNESS (Pts) + 5 (Max) + 5 (Max)
--- TENSILE STRENGTH (%) ± 20 (Max) ± 20 (Max)
--- ELONGATION AT BREAK (%) ± 30 (Max) ± 30 (Max)
VOLUME SWELL : AT 70º C FOR 72 HRS/IN ASTM D 471
IRM OIL NO.1 NOT RECOMMENDED NOT RECOMMENDED
IRM OIL NO.2 NOT RECOMMENDED NOT RECOMMENDED
IRM OIL NO.3 NOT RECOMMENDED NOT RECOMMENDED
POLYMER CONTENT (EPDM) 10% 10%
CHEMICAL RESISTANCE
--- OZONE FAIR ASTM D 1149 FAIR
--- DILUTE ACIDS AND BASES FAIR FAIR
--- CONCENTRATED ACIDS AND BASES NOT RECOMMENDED NOT RECOMMENDED
--- OILS NOT RECOMMENDED NOT RECOMMENDED
--- SOLVENTS NOT RECOMMENDED NOT RECOMMENDED
TEMPERATURE RANGE -30 º to +90º C -30 º to +90º C
COLOUR BLACK BLACK