| PROPERTIES | TEST METHOD | VALUES FPS UNITS | TEST METHOD | VALUES METRIC UNITS |
| SPECIFIC GRAVITY | DIN 53508 | 1.17±0.05 | ASTM D297 | 1.17±0.05 |
| HARDNESS | DIN 53505 | 60 ± 5 SH A | ASTM D2240 | 60 ± 5 SH A |
| TENSILE STRENGTH ( MIN ) | DIN 53504 | 1638 PSI | ASTM D412 | 115 KG/CM2 |
| ELONGATION AT BREAK ( MIN ) | DIN 53504 | 450% | ASTM D412 | 450% |
| ABRASION RESISTANCE ( MAX ) | DIN 53516 | 120 MM3 | ASTM D5963 | 120 MM3 |
| COMPRESSION SET (70ºC/24 HRS/25% COMPRESSION) (MAX) | DIN ISO 815-1 | 30% | ASTM D395 METHOD B | 30% |
| TEAR RESISTANCE ( ANGULAR ) MIN | DIN 53515 | 168 LBS/INCH | ASTM D624 | 30 KG/CM |
| ANTISTATIC CHARACTERISTIC | ASTM D257 | 105 to 109 | ASTM D257 | 105 to 109 |
| CHANGE IN PROPERTIES AFTER | ||||
| HEAT AGEING FOR ( 72 HRS. AT 70ºC ) | ASTM D573 | |||
| — HARDNESS (PTS) | + 5 (MAX) | + 5 (MAX) | ||
| — TENSILE STRENGTH (%) | + 10 / – 25 | + 10 / – 25 | ||
| — ELONGATION AT BREAK (%) | + 10 / – 25 | + 10 / – 25 | ||
| VOLUME SWELL : AT 70ºC FOR 72 HRS | ASTM D 471 | |||
| IN IRM OIL NO.1 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| IN IRM OIL NO.2 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| IN IRM OIL NO.3 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| CHEMICAL RESISTANCE | ||||
| — OZONE | FAIR | ASTM D 1149 | FAIR | |
| — DILUTE ACIDS AND BASES | GOOD | GOOD | ||
| — CONCENTRATED ACIDS AND BASES | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — OILS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — SOLVENTS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| TEMPERATURE RANGE | -25º TO + 70ºC | -25º TO + 70ºC |